STUDI KOROSI PADA PADUAN FERRONICKEL DALAM LINGKUNGAN KLORIDA

Maman Kusman, Agus Solehudin
Abstrak
Ketahanan korosi dari paduan ferronickel telah diteliti. Spesimen dihasilkan dari proses peleburan pada tungku busur listrik dibawah kondisi atmosfir argon selama 4 jam untuk meningkatkan homogenitas. Spesimen dikarakterisasi menggunakan mikroskop optik dan SEM-EDS. Sifat mekanik paduan paduan ferronickle diuji dengan menggunakan mikrohardness tester. Karakterisasi paduan ferronickle hasil peleburan (as cast) menggunakan mikroskop optik memperlihatkan bahwa semua spesimen mengandung mikrostruktur granular, dan memipih halus pada struktur mikro spesimen setelah heat treatment. Karakterisasi mikrostruktur pada sebagian spesimen as cast mengandung porositas. Hasil uji kekerasan memperlihatkan bahwa kekerasan meningkat seiring dengan meningkatnya kandungan Cr pada paduan. Hasil uji korosi memperlihatkan bahwa laju korosi menurun seiring dengan kandungan Cr pada paduan.

Kata kunci : korosi, klorida, chrom, ferronickle, SEM-EDS

ABSTRACT
Corrosion resistance of ferronickel alloy has been investigated. Specimens produced from the smelting process in electric arc furnace under argon atmosphere for 4 h to improve homogeneity. Specimens were characterized using optical microscopy and SEM-EDS. The mechanical properties of ferronickel alloy were tested using micro hardness tester. Characterization of ferronickel alloy smelting results (as cast) using an optical microscope showed that all specimens contain granular microstructure, while the microstructure of specimens after heat treatment form flattened smooth. The microstructure of as cast specimens contain some porosity. Hardness test results showed that hardness increases with increasing Cr content in the alloy. Corrosion test results showed that the corrosion rate decreases with Cr content in the alloy.

Keywords: corrosion, chloride, chrome, ferronickel, SEM-EDS